# Introduction iTi shape memory alloys (SMA) are a unique class of metals that show non-diffusional phase transformation in the solid state induced by temperature changes and/or mechanical loads [1][2][3], differently of conventional engineering metals. The shape memory properties combined with the good corrosion resistance and biocompatibility of the NiTi shape memory alloys make them high attractive to smart engineering applications, such as Micro-Electro-Mechanical-Systems (MEMS). On the other hand, these alloys present great problems of machining and conformability that limit their applications. Thus welding techniques appears as a viable technological alternative to obtain complex geometry components made of shape memory alloys [4,5]. Joining NiTi SMA by fusion welding processes is a technological challenge due to the formation of fragile intermetallic compounds, which leads to a intense loss of tenacity in the welded joints, due to solidification cracks associated with the dendritic microstructure of the weld metal. In addition, precipitation of deleterious phases in the thermally affected zone and in the weld metal can result in severe reduction of mechanical resistance [6][7][8][9][10]. Solid state welding processes, like friction stir welding (FSW), are a technical alternative to join these alloys because no precipitation of brittle intermetallic compounds occurs [11]. # II. # Materials and Methods In this paper an austentic NiTi shape memory thin sheet was used. Table 1 shows the chemical composition of the sheet, according to Sunrise Titanium Technology Co. Ltd. Tab.1: Chemical composition of thin sheets (wy.%) Ti (%) Ni (%) 44,09 55,91 After previous studies, the FSW process parameters used was 180 mm/min welding travel speed and rotation of tool tip of 1500 rpm. A 4-axis HOMI machining center was used to fabricate the welded joints. The tool shoulder diameter is 17 mm and the tip diameter is 2mm. The phase transformation temperature was determined by variation of the electrical resistance as a function of the temperature (ERT) [2] with an average heating or cooling rate of 4°C/min cooling from 100°C to -60°C and then heating to 100°C. The microhardness measurements were performed using a microindenter model FM-700 from Future Tech, applying a load of 50 gf for 15 seconds with a distance between the indentations approximately of 200 µm. Tensile tests were performed on an MTS 810 testing machine with a displacement rate of 0.05mm/min at room temperature. The fracture surfaces were observed by scanning electron microscopy (SEM) using a TESCAN microscope, VEGA 3 SBH model. # III. # Results and Discussion Fig. 1 shows the percentage variation curves of the electrical resistance as a function of temperature (ERT), using the temperature of 100°C as the austenitic reference state. The profile of the curve in the friction stir welded condition indicates, qualitatively, that the material will be in the austenitic state at room temperature (about 25°C). It is only possible to identify a slight inflection of the ERT curve, indicating possible temperature of beginning of the R phase transformation (Rs) from phase. This behavior is similar to that of NiTi SMA alloys that have been subjected to cold or hot rolling, which phase transformation are blocked due to the characteristic hardening of this manufacturing process [2,11]. The R phase is a transition state between the austenitic and martensitic phases of NiTi SMA characterized by a trigonal crystalline structure with rhombohedral distortion [12]. Fig. 2 shows the Vickers microhardness profile of the welded joint. It is possible to verify that the hardness in the stir zone is higher than the base metal, due to the mechanical work of the FSW process, which promotes grain refining and consequent increase of resistance [11]. In Fig. 3 it is possible to observe the stressstrain behavior of NiTi SMA welded joint. The welded joint showed satisfactory mechanical resistance [13,14,15], reaching a ultimate tensile strength of 700 MPa and 13% strain, higher than those observed by other authors that utilized fusion welding processes [5,7,16,18,19,20,21,[22][23][24][25][26] and equal to those who used solid state welding processes [11,27] except Shinoda et al [28]. # Conclusion In this paper thin sheets of NiTi SMA were welded by FSW process. The welded joint obtained by this process presented good mechanical properties and it was capable of achieve 700 MPa ultimate tensile strength and 13% strain. The welded joint remained in the austenitc phase state after welding, differently of fusion welding process. The stress induced martensite occurs at 450 MPa in the welded condition, 50 MPa above the base metal. The increase in mechanical resistance in detriment of ductility observed indicates that hardening occurs in function of the mechanical work of the friction stir welding process. 1![Fig.1: Variation of electrical resistance as a function of temperature (ERT) in NiTi FSW condition and the base metal (BM)](image-2.png "Fig. 1 :") 2![Fig.2: Vickers microhardness profile of the welded joint](image-3.png "Fig. 2 :") 3![Fig.3: Stress-strain behavior for NiTi SMA friction stir welded joint Fig.4 shows the aspect of the fracture surface of the welded joint. The fracture occurred near the center of the stir zone presenting ductile characteristics, such as dimples due to large deformations achieved.](image-4.png "Fig. 3 :") 4![Fig.4: Fracture surface of the friction stir welded joint IV.](image-5.png "Fig. 4 :") © 2017 Global Journals Inc. (US) * Shape Memory Alloys: Modeling and Engineering Applications DCLagoudas 2008 Springer Texas * Shape Memory Materials KOtsuka CMWayman 1998 Cambridge University Press Cambridge, UK * JMJani MLeary ASubic MAGibson * Mater Des 56 2014 * Design of Shape Memory Alloys (SMA) Actuators ARao ARSrinivasa JNReddy 2012 Springer Texas * Microstructural investigations of laser welded dissimilar nickeltitanium-steel joints HGugel WTheisen Proceedings 8th European symposium on martensitic transformations 8th European symposium on martensitic transformations 2009 * Plasma Welding of NiTi to NiTi CVan Der Eijk HFostervoll ZSallom OMAkselsen Stainless Steel and Hastelloy C276, Int. Conf. Joining of Specialty Materials VI Program, ASM Materials Solutions Conf. & Exposition Pittsburgh, PA, USA 2003 * AFalvo FMFurgiuele CMaletta Mat Sci Eng A 412 2005 * AIkai KKimura HTobush Journal of Intelligent Material Systems and Structures 7 1996 * WHGong YHChen LMKe Trans Nonferrous Met Soc China 21 2011 * Annals of DAAAM for 2012 & Proceedings of the 23rd International DAAAM Symposium PVondrous LKolarik MKolarikova 2012 Vienna * Friction Stir Processing of Nitinol. Friction Stir Welding and Processing III BLondon JFino A RPelton MMahoney 2005 Warrendale * PLukás PSittner DLugovoy DNeov MCeretti Appl. Phys. A 74 2002 * Avaliação das Propriedades Termomecânicas de Fios de Liga com Memória de Forma NiTi Soldados por Pulsos de Micro TIG FernandoAmorim Andrade Soldag. insp 20 4 2015 * GRMirshekari ASaatchi AKermanpur SKSandrnezhaad Optics & Laser Technology 54 2013 * Tungsten Inert Gas (TIG) welding of Ni-Rich NiTi plates: functional behavior JPOliveira DBarbosa BrazFernandes FMMiranda RM Smart Materials and Structures 25 * Plasma Welding of NiTi to NiTi CVan Der Eijk HFostervoll ZSallom OMAkselsen Stainless Steel and Hastelloy C276, Int. Conf. Joining of Specialty Materials VI Program, ASM Materials Solutions Conf. & Exposition Pittsburgh, PA, USA 2003 * CWChan HCMan FTCheng Mat Sci Eng A 559 2012 * Effect of ageing treatment on the transformation behavior of Ti-50.9 at.% Ni alloy YZheng FJiang LLi HYang YLiu Acta Materialia, v 56 2008 * Annals of DAAAM for 2012 & Proceedings of the 23rd International DAAAM Symposium PVondrous LKolarik MKolarikova 2012 Vienna * Laser welding of NiTi shape memory alloy wires and tubes for multi-functional design applications ZZeng MYang JPOliveira DSong BPeng Smart Materials and Structures 25 2016 * Laser welding of Shape Memory Alloys. Dissertação de mestrado submetida a Lisboa LMVieira 2010 Portugal Universidade Nova de Lisboa * Laser welding of Ni-rich TiNi shape memory alloy: mechanical behavior PSchlossmacher THaas ASchussler Journal de Phsyique 4 7 1997 * YGSong WSLi LLi YFZheng Mat. Let 62 2008 * Laser welding of NiTi orthodontic archwires for selective force application PSevilla FMartorell CLibenson JPlanell FGil Journal of Materials Science: Materials Medical 19 2008 * MIKhan SKPanda YZhou TMater Jim 49 2008 * XKZhao LLan HSun JHHaung HZhang YWang Materials Letters 64 2010 * Review of Progress in Quantitative Nondestructive Evaluation, v. 30 SMeir SGordon MKarsh AWiezman RAyers DLOlson 2011 * Transactions of the TShinoda TTsuchiya HTakahashi 1991 Japan Welding Society 22