# I. Introduction elf-compacting concrete (SCC) and selfcompacting fiber reinforced concrete (SCFRC) are special types of concrete mixture that is characterized by resistance to bleeding and segregation. SCC can be cast without need to using vibration machine or compaction. Products made with SCC have high quality, excellent finish, and are virtually free of flaws, such as large voids, because of the excellent filling ability of SCC without honeycomb formation (Okamura and Ouchi, 2003;Brouwers and Radix, 2005;Nanthagopalan and Santhanam, 2011). SCC is produced with the addition of fine industrial wastes, including fly ash (FA), silica fume, and furnace slag (Siddique, 2011). FA and some types of pozzolanic materials have been successfully used as mineral admixtures in SCC (Gesoglu and Ozbay, 2007;Ramanathan et al., 2013). The addition of mineral admixtures results in the sufficient viscosity of SCC, consequently reducing bleeding, segregation, and plastic shrinkage. In addition to fine mineral admixtures, agricultural waste materials, including palm oil fuel ash or rice husk ash, can be used as admixtures in SCC (Safiuddin et al., 2011;Mohammadhosseini et al., 2015). FA is added to concrete mixtures to prevent segregation and bleeding, increase flowability, and control hardened concrete properties, including compressive, indirect tensile, and flexural strengths (Siddique, 2012;Ashtiani et al., 2013;Celik et al., 2014;). The use of FA in SCC production requires the addition of a superplasticizer (SP) to the concrete mix to achieve high workability and appropriate mix proportions. A high SP dosage, however, increases bleeding and segregation in fresh concretes. These problems can be avoided by adding a viscosity-modifying admixture (VMA) to increase the viscosity of fresh concretes. Furthermore, the use of fine mineral admixtures can reduce the amount of SPs required to achieve the desired rheology. Moreover, the use of FA as an alternative material reduces the need for VMAs ( Ouchi et al., 1997;Cyr and Mouret, 2003;Feleko?lu et al., 2007). Nevertheless, replacing the fine mineral admixtures of cement mass, especially at high mass replacement, affects the characteristics of SCCs because of the variations in cement mass and in water/cement ratio. The addition of fibers improves the flexural strength, toughness, and tensile strength of concrete. Numerous researchers have reported that adding fibers at volumetric ratios of 0.1% to 1.0% improves the strength and engineering properties of ordinary concrete (Mohamed, 2006;Banthia and Gupta, 2006;Al Qadi et al., 2011;Islam and Gupta, 2016). The addition of fibers to concrete, however, has negligible effects on compressive strength and the modulus of elasticity. Moreover, the workability and flowability of SCRFCs decrease upon the addition of polypropylene fibers (PFs). The reduction of SCRFC workability due to the addition of fibers depends on many parameters, such as fiber type, dosage, and shape (Corinaldesi and Moriconi, 2011;El-Dieb and Taha, 2012). FA has been successfully added to SCC at replacement rates of up to 60% cement mass, and at a replacement rate of 35% cement mass to cement mixtures without the inclusion of PFs. Previous studies on the properties of SCCs have reported that replacing 30% of cement mass with FA produced concretes with excellent flowability and workability without the addition of fibers. The goal of the present investigation is to study the properties of fresh and hardened SCC and SCRFC. In this study, FA was added at replacement rates of 0%, 20%, 40%, and 60% cement mass. Then, PFs were added to the cement mixtures at a volumetric ratio of 0.22% to produce SCFRC. Segregation, bleeding, slump flow, slump flow T50, L-box V-funnel T5, and V-funnel tests were conducted on fresh concrete. In addition, the compressive, flexural, and tensile strengths of hardened concrete at ages 7, 14, 28, and 90 days were investigated. # II. Materials and Methods # a) Materials The tests carried out in order to study behavior the SCC during states the fresh and hardened concrete with (SCCF) and without polypropylene. The Slump flow, slump flow T50, L-box V-funnel T5, V-funnel, segregation and bleeding tests are conducted during the fresh state. After casting then curing concrete samples in the water basin until the ages of testing, compressive, tensile and flexural strength tests have been carried out. Production of the SCC and SCCF requires application stringent on materials selecting and its quality, also determine the proportions all of the ingredients according to the mix design method, taking into consideration. # b) Cement Ordinary Portland cement (OPC) was used in the present investigation. Cement characterization tests were conducted in accordance with ASTM C150 (ASTM, 2004). Tables 1 and 2 shown the chemical composition and physical characteristics of cement respectively. A crushed basalt rock with a maximum size of 12.7 mm was used as a coarse aggregate (CA), and natural sand was used in the concrete mixtures as a fine aggregate (FA). The CA and FA had a specific gravity of 2.63 and 2.71, and water absorptions of 0.6 and 0.9 % respectively. # e) Fine Aggregate The particle shapes and grade of FAs are important factors in SCC production. In this investigation, natural sand, which conforms to ASTM C33 specification, (ASTM, 2004) was used. Table 4 shows the grading analysis of FA. # f) Coarse Aggregate Table 4 shows that the grade of the CA, which conforms to the ASTM C33 specifications (ASTM, 2004). # Table 4: Grading of Coarse and Fine Aggregate g) Polypropylene fibers In this paper, 12 mm PFs were used, some of their physical properties are provided in Table 5. # Oxides # i) Mix design methods Mix design methods for SCC differ considerably from the regular conventional concrete design. There are many mix design methods. Estimating the required batch weights involves sequence of steps. These steps fit a proportioning procedure that covers a combination of: selection of aggregate to provide the desired passing ability; a cementitious (powder)/water ratio and mortar-paste fraction ratio that have been historically proven to produce SCC with the required slump flow; and stability. These steps, in combination with the addition of the appropriate admixture technology, should yield a trial batch with the desired fresh SCC properties. The following is a summary of steps for determining performance requirements and proportioning of SCC mixes. Step 1: Determine slump flow performance requirements; Step 2: Select coarse aggregate and proportion; Step 3: Estimate the required cementitious content and water; Step 4: Calculate paste and mortar volume; Step 5: Select admixture; Step 6: Make trial batch mixtures; Step 7: Test. When assessing the workability attributes of SCC (stability, filling ability, and passing ability), the slump flow test as well as a test to evaluate stability and passing ability (such as column segregation, or L-box) should be run; and Step 8: Adjust mixture proportions based on the test results and then re-batch with further testing until the required properties are achieved. The proportions of the concrete mixtures are summarized in Table 6. The preliminary investigations of this study include evaluation of the equipment and test procedures, evaluation of the mixture proportioning method chosen, mixing procedure and replacement of the FA, PF and dosage of superplasticizer. Testing for these initial investigations is limited on fresh concrete properties. # k) Mixing and casting of specimens In this investigation, the required quantities of materials were weighed for the correct mixing proportions. Then, cement was mixed with fly ash. The mixture was added to the coarse and fine aggregates. Then, all of the materials were mixed while dry for two minutes. Water was added to the mixtures in two stages: Half of the amount of water was initially added at the start of concrete mixing. The remaining water was then added after 30 s of concrete mixing. To obtain a homogeneous mixture, the concrete was continuously mixed for three min after the addition of water. After carrying out tests for fresh properties, mixing was immediately followed by casting. The specimens were removed from molds after 24 h of storage under laboratory conditions. Storage conditions were in accordance with ASTM C192. # III. Testing of the Samples a) Fresh concrete tests For determining SCC properties at fresh concrete state, the slump flow, slump flow T50, V-funnel, V-funnel T5, L-box, segregation and bleeding tests were applied. In order to reduce the influence of workability loss on tests' results of concrete samples, properties of fresh concrete were determined within 20 minutes of adding water. ? The Flow test was performed in according with the European Guidelines for Self-Compacting Concrete (EFNARC) standards (Concrete, 2005). Flow test using the cone, which allows the flow and movement of the SCC of unimpeded to can be characterized. It includes measuring slump flow diameter (D) after lifting the concrete cone, and in the same time measuring the time taken the concrete to spread in diameter 50 cm (T50). ? V-funnel test was performed in according with EFNARC standards .V-funnel is used to evaluate the fluidity, pass ability and segregation of selfcompacting concrete. The test time of V-Funnel is the time in seconds from the opened the outlet at the in the bottom the device until seen the light from above. In order get good properties in a fresh concrete of SCC, it requires to have test time between 6 to 12 second. ? L-box test was performed in according with EFNARC standards. L-box is used to assess the possibility of obstruction the filling capacity of the concrete in a confined construction elements. The filling capacity, determined as the ratio of the height the concrete in H2 at end of L-box with H1 at exit outlet (H1/H2), the ratio must be higher than 0.8. Figures 1 a, b, c and d show fresh concrete tests. ? The segregation test is carry out by filling the concrete into a cylinder a 66 cm high and diameter of 20 cm, which has split into three parts. The first part from the bottom is 16.5 cm in height, the middle section is 33 cm in height and the top part is 16.5 cm in height. After filling the apparatus left the concrete undisturbed or movement for 15±1 minutes, then collecting the concrete in the top and bottom parts and washed over a sieve a 4.75 mm to maintain the CA. The relative weight of CA in the top and bottom of the apparatus is used as an indication of resistance the segregation. ? Bleeding test was carried out on ASTM C 232. with maintaining the surrounding temperature of 18 to 24°C. Immediately record the mass of the container and its contents. Then place the container on a level platform free of vibration and cover the container to inhibit evaporation the water of the concrete sample. Must keep the cover of the container during time of the test. Water suction by pipet or similar instrument the, the accumulated water on the surface, at every 10-min through the first 40 min then at every 30 min thereafter until cessation of bleeding. # IV. Results and Discussion # a) Properties of fresh concretes The results of the slump flow test are presented in Table 7. The results represent the maximum spread (the final diameter of slump flow) and T50, the time required for the concrete flow to fill a 50-cm-diameter circle. EFNARC recommends that concrete mixtures should have slump flow diameters of 55 cm to 75 cm to 2002). Slump flow that exceeds a 75-cm diameter may cause concrete to segregate, whereas that with less than a 55-cm diameter may indicate concrete with flow rates that are insufficient for passing through an overcrowded reinforcement. The results showed that concrete mixtures with PF (SCFRC) and without PF (SCC) and with the addition of FA at replacement rates of 20% and 40% cement mass met the slump flow flow rates increased by 40% and 34% when FA was added at replacement rates of 20% and 40% cement mass, respectively. The workability and flowability of all SCRFC mixtures were lower than those of all SCC the slump flow rates of SCFRCs decreased by 21%, 12%, and 17% when FA was added at replacement rates of 0%, 20%, and 40% cement mass, respectively. In general, increasing the replacement rates of FA from 20% to 40% cement mass did not significantly decrease the workability of concrete. Adding FA to cement at a replacement rate of 06% has a negative effect on properties of SCC. # Table 7: Results of Slump flow Tests In addition to the slump flow test and slump flow T50, the V-funnel test was conducted to estimate the flowability of SCC and SCFRC mixtures. The V-funnel flow time was calculated in seconds between the time of the beginning of opening the bottom outlet until the light became noticeable from the bottom outlet. EFNARC recommends that concretes should have V-funnel flow times of 6 s to 12 s and a L-box ratio H2/H1 greater than 0.80 to be considered as SCCs (EFNARC, 2002). Table 8 shows the results of V-funnel test and Lbox. The results indicated that SCC and SCFRC mixtures that contained FA at replacement rates of 20% and 40% cement mass met the requirements for SCC. By contrast, SCC and SCFRC mixtures that contained FA at replacement rates of 0% and 60% cement mass did not meet the requirements for SCC. The decrease in the passing and filling abilities SCCs likely resulted from the high volume of added FA. Moreover, all SCRFC mixtures had lower passing and filling abilities than SCC mixtures. SCC and SCFRC mixtures containing FA at a replacement rate of 60% cement mass did not pass the V-funnel and L-box V-funnel T5 tests. The results suggested that increasing the replacement rate of FA to 60% cement mass exerted the greatest negative effect on the passing and filling abilities of the cement mixtures. Table 8: Results of L-box and v-funnel tests requirements for SCCs. Concrete mixtures with the addition of FA at replacement rates of 0% and 60% cement mass exhibited low slump flow. Moreover, the results showed a wide range of variations, illustrating the effects of FA replacement rates and PF addition on SCC and SCRFC flowability. The decrease in the workability and flowability of SCC may be attributed to the addition of a high volume of FA as an alternative material. Slump mixtures. Moreover, the flowability SCC and SCFRC mixtures that contained FA at replacement rates of 0% and 60% cement mass did not meet the minimum requirements of the T50 test. Results also showed that Table 9 shows the results of the bleeding and segregation tests. SCC and SCFRC mixtures that contained FA at replacement rates of 20% or 40% cement mass had high rates of bleeding and segregation. By contrast, SCC and SCFRC mixtures that contained FA at replacement rates of 0% or 60% cement mass had the lowest rates of bleeding and segregation. The addition of a high volume of FA likely decreased the bleeding and segregation of SCCs. Furthermore, the bleeding and segregation rates of SCFRC mixtures were lower than those of SCC mixtures. , 3, and 4 show the compressive strength test results for SCC and SCRFC at ages 7, 14, 28, and 90 days. Results showed that the evolution of compressive strength varied in SCC and SCRFC. The decline in compressive strength became apparent when FA replacement ratio increased to 60% cement mass. The decline in the compressive strength of SCC and SCRFC may be attributed to the addition of FA at the high replacement rate of 60% cement mass, which introduced air bubbles in hardened concrete and decreased compressive strength. The best compressive strength of SCCs at ages 7, 14, 28, and 90 days was obtained when FA was added at the replacement rate of 20%. The compressive strength of SCCs increased by 16.1%, 7.4%, 3.9%, and 1.2% at ages 7, 14, 28, and 90 days, respectively, when FA was added at the replacement rate of 20% cement mass. In addition, the compressive strength of SCCs increased by 8.5% and 1.5% at ages 7 and 82 days, respectively, when FA was added at the replacement rate of 40% cement mass. Compressive strength decreased by 18.8%, 24.1%, 15.9%, and 11.8% at ages 7, 14, 28, and 90 days, respectively, when FA was added at the replacement rate of 60% cement mass. The compressive strength of SCRFCs s decreased compared with that of SCCs. Adding FA at the replacement rate of 60% cement mass greatly decreased the compressive strength of SCRFCs s. The percentages of decrease in compressive strength were higher in SCRFC mixtures. Thus, this finding may be attributed to the negative effect of fibers on concrete rheology, which affected the degree of concrete compaction and consequently decreased the compressive strength of concrete (Akinpelu et al., 2017). The following conclusions were drawn from the results of this study: 1. The addition of FA positively affected the properties of fresh concrete and the compressive strength of mixtures at all ages. 2. SCCs with and without PFs were obtained by adding FA at the replacement rates up to 40% cement mass. 3. The best SCC workability was obtained when FA was added at replacement rates of 20% and 40% cement mass without PFs. Fresh SCC samples with this formulation exhibited slump flow diameters of 73 cm and 70 cm; blocking ratios of 0.86 and 0.88; and flow times of 5.2 to 5.3 s. 4. Based on the test results, FA should be utilized to produce SCC with high strength at 90 days. Compressive strength reached 41 MPa when FA was added at replacement rates of 20% and 40% cement mass to SCC and SCRFC. 5. The addition of FA at different replacement ratios to SCC and SCRFC mixtures exerted different effects. Thus, for reasons of economy, FA should be added to SCCs and SCRFCs s at replacement rates of 20% to 40% cement mass. 6. The addition of PFs decreased the properties of fresh concrete but improved flexural and indirect tensile strengths. 1![Fig. 1: Fresh concrete test b) Hardened concrete tests In the state of hardened concrete, the tests that were carried out are compressive, indirect tensile and flexural strength. Compressive strength test according to ASTM C39 standard cubes measuring 150 x150 x 150 mm were used. Indirect tensile tests were carried out according to ASTM C496. The dimensions of the standard cylinder are 150 D x 300 H mm. Flexural tests were carried out according to ASTM C78. The dimensions of the standard prisms are 100 x100 x 400 mm. All tests were conducted at 7, 14, 28 and 90 days. The average value of the three specimens for each test age is determined and recorded.](image-2.png "Fig. 1 :") 1![Fig. 1(a): Slump flow T50 test Fig. 1(b): Slump flow test](image-3.png "Fig. 1 (") 2![Fig. 2: Results of Compressive Strength Test of SCC](image-4.png "Fig. 2 :") 34![Fig. 3: Results of Compressive Strength Test of SCCF](image-5.png "Fig. 3 :Fig. 4 :") 5![Fig. 5: Results of Indirect Tensile Strength Test of SCC](image-6.png "Fig. 5 :") 678910![Fig. 6: Results of Indirect Tensile Strength Test of SCCF](image-7.png "Fig. 6 :Fig. 7 :Fig. 8 :Fig. 9 :Fig. 10 :") 1 2c) Fly ashFA meets the general requirements of ASTMC618 Class F (ASTM, 2004). Table 3 presents thechemical composition and physical characteristics of flyash. 3d) Aggregate 5Content %ASTM C 618 Class F© 2017 Global Journals Inc. (US) 6PropertiesFPsFormWhite color fibersDensity0.91 kg/lFiber Length12 mmFiber Diameter18 micronSoftening point160 o CSpecific surface area200 m 2 / kgTensile strength (MPa)350 MPaj) Mixture proportions 9b) Compressive strengthFigures 2 © 2017 Global Journals Inc. (US) Year 2017EInfluence of Fly Ash on the Properties of Self-Compacting Fiber Reinforced Concrete * Evaluation of splitting tensile and compressive strength relationship of self-compacting concrete MAAkinpelu SOOdeyemi OSOlafusi FZMuhammed 10.1016/j.jksues.2017.01.002 Journal of King Saud University-Engineering Sciences 2017 * Effect of polypropylene fibres on fresh and hardened properties of self-compacting concrete at elevated temperatures AlQadi AMustapha KNagathan SAl-Kadi Q Australian Journal of Basic and Applied Sciences 5 10 2011 * Mechanical and fresh properties of high-strength self-compacting concrete containing class C fly ash MSAshtiani ANScott RPDhakal Construction and Building materials 47 10 2013 * American Section of the International Association for Testing Materials 2004 Pennsylvania, United States of America Annual book of ASTM standards * Influence of polypropylene fiber geometry on plastic shrinkage cracking in concrete NBanthia RGupta Cement and Concrete Research 36 7 2006 * Self-compacting concrete: theoretical and experimental study HBrouwers HRadix Cement and Concrete Research 35 11 2005 * A comparative study of selfconsolidating concretes incorporating high-volume natural pozzolan or high-volume fly ash KCelik CMeral MMancio PKMehta PJMonteiro Construction and Building materials 67 9 2014 * The European Guidelines for Self-Compacting Concrete Bibm 2005 London * Characterization of self-compacting concretes prepared with different fibers and mineral additions. Cement and Concrete Composites VCorinaldesi GMoriconi 2011 33 * Rheological characterization of superplasticized cement pastes containing mineral admixtures: consequences on self-compacting concrete design. The American Concrete Institute MCyr MMouret Special Publication 217 2003 * Specification and guidelines for self-compacting concrete, European Federation of National Associations Representing producers and applicators of specialist building products for Concrete EFNARC 2002 * Flow characteristics and acceptance criteria of fiber-reinforced selfcompacted concrete (FR-SCC) AEl-Dieb MRTaha Construction and Building materials 2012 27 * Effect of water/cement ratio on the fresh and hardened properties of self-compacting concrete BFeleko?lu STürkel BBaradan Building and Environment 42 4 2007 * Effects of mineral admixtures on fresh and hardened properties of self-compacting concretes: binary, ternary and quaternary systems MGesoglu EOzbay Materials and Structures 40 9 2007 * Evaluating plastic shrinkage and permeability of polypropylene fiber reinforced concrete GSIslam SDGupta International Journal of Sustainable Built Environment 5 2 2016 * Effect of polypropylene fibers on the mechanical properties of normal concrete RMohamed Journal of Engineering Sciences 34 4 2006 Assiut University * Influence of palm oil fuel ash on fresh and mechanical properties of self-compacting concrete HMohammadhosseini AAAwal AHEhsan Sadhana 40 6 2015 * Fresh and hardened properties of self-compacting concrete produced with manufactured sand. Cement and Concrete Composites PNanthagopalan MSanthanam 2011 33 * Self-compacting concrete HOkamura MOuchi Journal of advanced concrete technology 1 1 2003 * Effect of superplasticizer on self-compactability of fresh concrete MOuchi MHibino HOkamura Transportation Research Record: Journal of the Transportation Research Board 1574 1997 * Performance of selfcompacting concrete containing different mineral admixtures PRamanathan IBaskar PMuthupriya RVenkatasubramani KSCE journal of Civil Engineering 17 2 2013 * Flowing ability of the mortars formulated from selfcompacting concretes incorporating rice husk ash MSafiuddin JWest KSoudki Construction and Building materials 25 2 2011 * Properties of self-compacting concrete containing class F fly ash RSiddique Materials & Design 32 3 2011 * Properties of concrete made with volcanic ash. Resources, Conservation and Recycling RSiddique 2012 66