# I. Introduction entacene Field Effect Transistors (FETs) have been attractive for applications in the areas of Flexible display, RFIDs, sensors because its performances are similar to that of amorphous silicon thin film transistors [1][2][3][4][5]. Apart from these comparable electronic characteristics and promising low-cost fabrication, there are still important parameters of the device that needs better understanding and precise control for proper operation of the device. Some of the key issues are environmental stability, leakage current, threshold voltage and mobility [6][7][8][9][10][11][12]. In general organic FETs have higher threshold voltages than normally required for integrated circuit applications. The threshold voltage can depend on different factors such as gate bias stress [13,14], gate dielectric [15], and the thickness of the active layer material [16]. Properties of gate electrode and dielectric are also important parameters that affect the performance of the transistor. The dependence of threshold voltage on gate metal work function has also been reported [17,18]. In this paper we have simulated a top contact transistor and systematically studied the effect of gate work function and gate insulator thickness on channel parameters such as field, potential, charge concentration, threshold voltage, and field effect mobility. # II. Simulation where µ(E) is the field dependent mobility, µ0 is the zero field mobility, E is the electric field, ? is the zero field activation energy, ? is the electron Poole-Frenkel factor, k is the Boltzmann's constant, and T is the temperature. The Poole-Frenkel parameters extracted from the best match between simulation and experiment are ?=0.1, ?=3.58x10-5, and ?=10-5. Bottom contact pentacene Thin Film transistor is simulated and matched with experimental data, previously reported by our group [19][20][21]. Poole-Frenkellike electric-field dependence (equation below), which is the inverse variation in activation energy against the square root of electric-field strength [22,23], has been employed for pentacene active channel. Nonlinear transport organic semiconductor materials is intensively explained through Poole-Frenkel (PF) transport mechanism [24][25][26][27]. The model explains the temperature and electric-field dependencies of charge carrier drift mobilities in disordered materials. # III. Transistor Channel Parameter Simulation Results and Discussion A top contact device (Fig. 2) with a width of 100 µm and channel length of 10 µm is used for simulation. A 30 nm pentacene active layer and a 6 nm gate dielectric is used. The thickness of gold source drain contacts is 30 nm and that of aluminum gate electrode is 20 nm The change in threshold voltage associated with change in electrode work function and change in the flat band voltage is also expected. With no charge present in the oxide or at the oxide-semiconductor interface, the flat-band voltage simply accounts for the work function difference between the semiconductor and the metal gate. As has been reported [28], the effect of gate work function is significant, particularly when the transistor is biased at accumulation. The gate work function can affect both the gate leakage current and the source drain current. As shown in Fig. 3, the current increases by about a factor of 3 when the gate metal work function increases from 3.8 eV to 5.4 eV. accumulation, has also been examined. We probed the electric field at the interface between the gate insulator and pentacene for fixed drain voltage (-3 V). The change in the flat band voltage or the threshold voltage is also reflected in a change on the channel electric field and channel charge concentration. As shown in Fig. 5, simulation results indicate that there exists a built in field at zero gate voltage. For each gate voltage, higher work function gate electrodes create higher channel field. 7. The channel mobility is also higher for higher work functions. For lower work function gate electrodes, the mobility starts at very low value at zero gate voltage and increases with gate voltage. But for the higher work function electrodes, the mobility has a higher value at zero gate voltage. This is the result of the high electric field and charge density. Experimental studies in the literature indicate that channel mobility increases when the channel field and charge concentration increases [29]. We have extracted the mobility for different work Fig. 8: Channel potential at different positions along the channel from source to drain for different gate electrode work functions resistance of pentacene between the channel and the electrode [30]. This is attributed to low mobility or depletion near the contacts and Schottky barriers at the contacts [31,32]. The potential profiles are clearly nonlinear as seen in the figure. The nonlinearity of the potential profile is more pronounced near the drain electrode than near the source. This is due to the fact that the relative decrease of the induced charge density in the accumulation layer when going from source to drain as well as an associated decrease of the field effect mobility [33]. In going from the source (x=0) to the drain (x=12) along the channel, the potential drops fast for higher gate electrode work function. This faster drop of potential gradient is associated with the higher channel electric field we have observed at higher gate electrode work functions. # Global Journal of Researches in # b) Impact of gate dielectric thickness In addition to studying the impact of the work function on the channel properties, we have simulated devices at different gate insulator thicknesses to study its effect on channel field, channel charge concentration, threshold voltage, and channel charge mobility. As shown in Fig. 9 a, the field increases as the thickness of the dielectric decreases and this increase in field increases the charge accumulation in the channel (Fig. 9 b). However we haven't seen variation of the threshold voltage with thickness of the dielectric. This is because there is no variation of the flat band voltage, interface traps and charges as a function of the dielectric thickness. Fixed charge in the dielectric has not been included in our simulation model. To study the variation of the channel parameters The change in the thickness of the dielectric has also brought the change in the channel field effect mobility. Fig. 10 shows that the mobility variation with gate voltage and thickness of the dielectric. The mobility increases as a function of electric field only up to a little over the threshold voltage. After the channel is fully formed, the mobility starts to drop as the gate voltage increases to a more negative value. The drop is significant for lower dielectric thicknesses. Increasing the gate voltage increases both the electric field and the channel charge concentration. We have also shown this by simulating the device at a gate voltage of -3 V and dielectric thickness of 6 nm for various values of dielectric constant. The extracted mobility versus channel charge density is shown in Fig. 11. The figure shows an increase of mobility with channel charge density. So the decrease in mobility we observed in Fig. 10 at more negative gate voltages, with the decrease in dielectric thickness, should be from the high electric field strength. This is because the lower the dielectric thickness the higher the field and the higher the impact on mobility. Fig. 11: Channel mobility vs channel charge concentration # Global # Global # IV. Conclusion In summary, our simulation results show an impact of the gate metal work function and the gate dielectric thickness on channel field, channel potential, channel charge concentration, and mobility of the device. When the high work function gate electrode is used, there exists a built in field in the transistor channel. As the result there exist built in channel charge concentration and increased channel mobility at zero gate voltage. As expected, when the gate insulator thickness decreases the vertical electric field and the channel charge density increases. This increase in field and charge concentration slightly increases the mobility and the drain current. The field effect mobility decreases as the thickness of the dielectric decreases. The threshold voltage changes with gate electrode work function but remains the same when the thickness of the dielectric changes. The threshold voltage has changed from -1.3 V to -0.07 V by changing the work function from 3.8 eV to 5.4 eV. We also have seen a potential drop at the electrode/polymer interface and a nonlinear decrease in potential from source to drain. # Global 5![a) shows the characteristic family of curves of pentacene TFT for gate voltages 5 -20 volts in Global Journal of Researches in Engineering ( ) Volume XVI Issue VIII Version I Simulation based Characterization of the Simulation based Characterization of the Transport Channel Parameters of Pentacene Thin Film Transistor: Effect of Gate Insulator Thickness and Gate Electrode Work Function ? ?](image-2.png "Figure 5 (") 1![Fig. 1: ID -VD plots of the transistor (a); ID -VG plots of the transistor (b)](image-3.png "Fig. 1 :") 1.0x10 194x10 7Gate dielectric thicknessGate dielectric thichness (nm)66Channel field (V/cm)0 1x10 7 2x10 7 3x10 712 18 24-3 ) Channel charge concentration (cm0.0 2.0x10 18 4.0x10 18 6.0x10 18 8.0x10 1812 18 24Year 2016-3.0-2.5-2.0 Gate voltage (V) -1.5-1.0-0.50.0-3.0-2.5-2.0 Gate voltage (V) -1.5-1.0-0.50.06(a)(b)( ) Volume XVI Issue VIII Version I F of Researches in Engineering/V-s) Channel mobility (cm 20.660 0.665 0.670 0.655 0.625 0.630 0.635 0.640 0.645 0.650-30-25 Gate idielectric thickness (nm) -20 -15 6 12 18-10-50JournalGate voltage (V)© 2016 Global Journals Inc. (US) © 2016 Global Journals Inc. (US) ## V. Acknowledgments We gratefully acknowledge DOD for support of this work. We also wish to thank the fabrication group at UTD for provided stimulating discussions which motivated this study. * Organic thin-film transistors: A review of recent advances CDDimitrakopoulos DJMascaro IBM J. RES & DEV 45 11 2001 * HJKim SJKang DSPark KBChung MNoh CNWhang MHCho Characterization of a Pentacene Thin-Film Transistor with a * HfO2/Al2O3 Gate Insulator 2004 45 935 * High performance organic transistor active-matrix driver developed on paper substrate BPeng XRen ZWang XWang RCRoberts PK LChan September 2014 * High-Performance Pentacene Thin-Film Transistor With High-? HfLaON as Gate Dielectric CYHan WMTang CHLeung CMChe PTLai IEEE Electron Device Lett 34 11 2013 * Pentacene-Based Organic Thin Film Transistors for Ammonia Sensing H.-WZan W.-WTsai YLo Y.-MWu Yang Y.-S IEEE Sensors Journal 12 2012 * Environmental stability and electronic transport of pentacene thin film transistors DKnipp TMuck ABenor VWagner Journal of Non-Crystalline Solids 352 1774 2006 * Polymer Gate Dielectric Surface Viscoelasticity Modulates Pentacene Transistor Performance CKim AFacchetti TJMarks Science 318 76 2007 * Highperformance and low-voltage pentacene thin film transistors fabricated on the flexible substrate CSKim SJJo JBKim SYRyu JHNoh HKBaik SJLee KMSong Semicond. Sci. Technol 22 691 2007 * High-mobility polymer gate dielectric pentacene thin film transistors HKlauk MHalik UZschieschang GSchmid WRadlik WWeber J. Appl. Phys 92 5259 2002 * Thin-Film Transistors CRKagan Andry P 2003 334 New York * Leakage current reduction in pentacene-based thin References Références Referencias film transistor using asymmetric source/drain electrodes M.-HLim I.-YLee S.-GJeong JLee W.-SJung H.-YYu G.-HKim YRoh J.-HPark Organic Electronics 13 1056 2012 * Identifying orthogonal solvents for solution processed organic transistors AMGaikwad YKhan AEOstfeld SPandya SAbraham ACArias Organic Electronics 30 2016 * Light-induced bias stress reversal in polyfluorene thin-film transistors ASalleo RAStreet Journal of Applied Physics 94 471 2003 * Bipolaron mechanism for bias-stress effects in polymer transistors RAStreet ASalleo MLChabinyc Phys. Rev. B 68 85316 2003 * Pentacene thin film transistors on inorganic dielectrics: Morphology, structural properties, and electronic transport DKnipp RAStreet AVolkel JHo Journal of Applied Physics 93 347 2003 * Threshold voltage shift in organic field effect transistors by dipole monolayers on the gate insulator KPPernstich SHaas DOberhoff CGoldmann DJGundlach BBatlogg ANRashid GSchitter Journal of Applied Physics 94 6431 2004 * Theory and application of the material work function for chemical sensors, based on the field effect principle PBergveld JHendrikse WOlthuis Meas. Sci. Technol 9 1801 1998 * Self-consistent quantum-mechanical calculations in ultrathin siilicon-on-insulator structures TOuisse J. Appl. Phys 76 5989 1994 * SGowrisanker MAQuevedo-Lopez HNAlshareef BGnade SVenugopal RKrishna KKaftanoglu DAllee Organic Electronics 10 1217 2009 * SGowrisanker YAi HJia MAQuevedo-Lopez HNAlshareef ITrachtenberg HStiegler HEdwards RBarnett BEGnade Electrochemical and Solid-State Letters 12 3 2009 * WTWondmagegn NTSatyala RJPieper MAQuevedo-Lopez SGowrisanker HNAlshareef HJStiegler BEGnade J. Comput Electron 10 144 2011 * Temperature and electric-field dependence of the mobility of a single-grain pentacene field-effect transistor TMinari TNemoto SIsoda J. Appl. Phys 99 34506 2006 * ATLAS User's Manual March 2007 * Pentacene-Based Organic Field-Effect Transistors: Analytical Model and Simulation Methods versus Experiment Data MJSharifi ABazyar ACEEE Int. J. on Control System and Instrumentation 02 3 2011 * Nonlinear Transport in Organic Thin FilmTransistors with Soluble Small Molecule Semiconductor HKim D.-SSong J.-HKwon J.-HJung D.-KKim SMKim IMKang JPark H.-STae NBattaglini PLang GHorowitz J.-HBae Journal of Nanoscience and Nanotechnology 16 2016 * Cellulose-Derivative-Based Gate Dielectric for High-Performance Organic Complementary Inverters APetritz AWolfberger AFian TGriesser MIrimia-Vladu BStadlober Adv. Mater 27 2015 * Thin Films of Highly Planar Semiconductor Polymers Exhibiting Band-like Transport at Room Temperature JLee JWChung DHKim B.-LLee JPark SLee RHausermann BBatlogg S.-SLee IChoi WKim MSKang J. Am. Chem. Soc 137 2015 * Metal Gate Work Function Engineering on Gate Leakage of MOSFETs YHou I MLow TKwong D IEEE Transactions on Electron Devices 51 1783 2004 * CDDimitrakopoulos SPurushothaman JKymissis ACallegari JMShaw Low-Voltage Organic Transistors on Plastic Comprising High-Dielectric Constant Gate Insulators 1999 283 822 * Scanning Kelvin probe and photoemission electron microscopy of organic source-drain structures KMuller AGoryachko YBurkov CSchwiertz MRatzke JKoble Reif JSchmeißer D Synthetic Metals 146 2004 * Investigation of bottom-contact organic field effect transistors by two-dimensional device modeling TLi PPRuden IHCampbell DLSmith J. Appl.Phys 93 4017 2003 * Surface potential profiling and contact resistance measurements on operating pentacene thin-film transistors by Kelvin probe force microscopy KPPuntambekar PVPesavento CDFrisbie Appl. Phys. Lett 83 5539 2003 * Noncontact potentiometry of polymer field-effect transistors LBurgi HSirringhaus RHFriend Appl. Phys. Lett 80 2913 2002